Dual effect synergistically triggered Ce:(Y,Tb)3(Al,Mn)5O12 transparent ceramics enabling a high color-rendering index and excellent thermal stability for white LEDs

Ce:Y₃Al₅O₁₂ transparent ceramics (TCs) with appropriate emission light proportion and high thermal stability are significant to construct white light emitting diode devices with excellent chromaticity parameters. In this work, strategies of controlling crystal-field splitting around Ce³⁺ ion and doping orange-red emitting ion, were adopted to fabricate Ce:(Y,Tb)₃(Al,Mn)₅O₁₂ TCs via vacuum sintering technique. Notably, 85.4 % of the room-temperature luminescence intensity of the TC was retained at 150 °C, and the color rendering index was as high as 79.8. Furthermore, a 12 nm red shift and a 16.2 % increase of full width at half maximum were achieved owing to the synergistic effects of Tb³⁺ and Mn²⁺ ions. By combining TCs with a 460 nm blue chip, a warm white light with a low correlated color temperature of 4155 K was acquired. Meanwhile, the action mechanism of Tb³⁺ ion and the energy transfer between Ce³⁺ and Mn²⁺ ions were verified in prepared TCs.     

Organic mesh template-based laminated object manufacturing to fabricate ceramics with regular micron scaled pore structures

A new aqueous slurry-based laminated object manufacturing process for porous ceramics is proposed: firstly, an organic mesh sheet is pre-paved as a pore-forming template before slurry layer scraping; secondly, the 2D pattern is built with laser outline cutting of the dried mesh–ceramic composite layer; finally, the pore structure is formed after degreasing and sintering. Alumina parts with porosities of 51.5 %, round hole diameters of 80 ± 5 μm were fabricated using 70 wt. % solid content slurry and 100 mesh nylon net. Using an organic mesh as the framework and template not only reduces the risk of damage of the green body but also ensures the regularity, uniformity and connectivity of the micron scaled pore network. The layer-by-layer drying method avoids the delamination phenomenon and improves the paving density. The new method can realize the flexible design of the pore structure by using various organic mesh templates.     

Agronomic performance of high oleic,low linolenic soybean in Tennessee

Soybean oil hydrogenation alters the linolenic acid molecule to prevent the oil from becoming rancid, however, health reports have indicated trans-fat caused by hydrogenation, is not generally regarded as safe. Typical soybeans contain approximately 80 g kg⁻¹ to 120 g kg⁻¹ linolenic acid and 240 g kg⁻¹ of oleic acid. In an effort to accommodate the need for high-quality oil, the United Soybean Board introduced an industry standard for a high oleic acid greater than 750 g kg⁻¹ and linolenic acid less than 30 g kg⁻¹ oil. By combing mutations in the soybean plant at four loci, FAD2-1A and FAD2-1B, oleate desaturase genes and FAD3A and FAD3C, linoleate desaturase genes, and seed oil will not require hydrogenation to prevent oxidation and produce high-quality oil. In 2017 and 2018, a study comparing four near-isogenic lines across multiple Tennessee locations was performed to identify agronomic traits associated with mutations in FAD3A and FAD3C loci, while holding FAD2-1A and FAD2-1B constant in the mutant (high oleic) state. Soybean lines were assessed for yield and oil quality based on mutations at FAD2-1 and FAD3 loci. Variations of wild-type and mutant genotypes were compared at FAD3A and FAD3C loci. Analysis using a generalized linear mixed model in SAS 9.4, indicated no yield drag or other negative agronomic traits associated with the high oleic and low linolenic acid genotype. All four mutations of fad2-1A, fad2-1B, fad3A, and fad3C were determined as necessary to produce a soybean with the new industry standard (>750 g kg⁻¹ oleic and <30 g kg⁻¹ linolenic acid) in a maturity group-IV-Late cultivar for Tennessee growers.     

高分子材料导热性能影响因素研究进展

介绍了高分子材料导热性能影响因素研究进展，重点阐释了聚合物基体的结构特性（链结构、分子间相互作用、取向、结晶度等）、导热填料（种类、含量、形态、尺寸等）以及制备方法等对高分子材料导热性能的影响。     

Influence of aluminum phosphate on the tribocorrosion performance of chemically bonded phosphate ceramic coatings

In this study, chemically bonded phosphate ceramic coatings (CBPCCs) with different contents of aluminum phosphate (AP) are prepared on stainless steel (AISI 304L). Differential scanning calorimetry, X-ray diffraction, contact angle test, and a tribocorrosion experiment are carried out to clarify the role of AP in the tribocorrosion performance of CBPCCs. The results show that, with the increase in the AP content, the enthalpy of curing increases because of the greater formation of the bonding phase AlPO₄. Both in static corrosion and in tribocorrosion, the corrosion current density of CBPCCs achieves the lowest value when the weight ratio of AP to polytetrafluoroethylene is about 0.78. Additionally, the influence mechanism of AP on tribocorrosion is clarified. AlPO₄ from the reaction between AP and Al₂O₃ has excellent mechanical properties and can enhance the wear resistance of CBPCCs by reducing the mechanical wear and the increased wear due to corrosion. The alumina particles wrapped by AlPO₄ can form a dense and smooth surface and change the direction of electrolyte propagation, which leads to the increase in the tribocorrosion resistance of CBPCCs.     

珠江口盆地珠一坳陷古近系高自然伽马砂岩形成机制及油气地质意义

运用放射性元素寻找油气是一种非常规油气勘探手段。近年来,在珠江口盆地珠一坳陷富烃凹陷周边古近系钻遇高自然伽马(GR)砂岩,其GR值(100~300 API)甚至大于同区泥岩的GR值(100~200 API)。为了弄清该特殊现象背后的地质意义,对珠江口盆地珠一坳陷古近系高自然伽马砂岩开展了铀(U)、钍(Th)、钾(K)等3种元素含量与GR值的相关趋势线分析,从井震特征、岩性特征及矿物成分特征等入手分析了砂岩GR值增高的主要原因及成因机制,探讨了放射性元素聚集的条件、运移通道、驱动力以及油气意义。结果表明:西江、惠州地区由U含量增高导致砂岩GR值偏高,恩平、番禺地区由K,Th含量增高导致砂岩GR值偏高;砂岩GR值增高有两大成因机制,一是地下流体带来的放射性元素离子U4+在氧化-还原面处富集后导致地层GR值偏高,这种特殊现象说明在具有连通基底大断裂旁的圈闭中,U4+的富集指示了曾经油气的存在,证实了研究区油气运移通道的有效性,对于油气藏的预测有着非常重要的指导性意义,二是地表流体带来的含放射性元素的矿物大量沉积后导致地层GR值偏高,含放射性元素矿物性质不稳定,可指示近源供给的存在,对于判断物源及沉积环境有着非常重要的意义。该研究成果为预测研究区油气成藏有利区带提供了依据。     

Microstructural and mechanical properties assessment of transient liquid phase bonding of CoCuFeMnNi high entropy alloy

The transient liquid phase (TLP) bonding of CoCuFeMnNi high entropy alloy (HEA) was studied. The TLP bonding was performed using AWS BNi-2 interlayer at 1050 °C with the TLP bonding time of 20, 60, 180 and 240 min. The effect of bonding time on the joint microstructure was characterized by SEM and EDS. Microstructural results confirmed that complete isothermal solidification occurred approximately at 240 min of bonding time. For samples bonded at 20, 60 and 180 min, athermal solidification zone was formed in the bonding area which included Cr-rich boride and Mn₃Si intermetallic compound. For all samples, the γ solid solution was formed in the isothermal solidification zone of the bonding zone. To evaluate the effect of TLP bonding time on mechanical properties of joints, the shear strength and micro-hardness of joints were measured. The results indicated a decrement of micro-hardness in the bonding zone and an increment of micro-hardness in the adjacent zone of joints. The minimum and maximum values of shear strength were 100 and 180 MPa for joints with the bonding time of 20 and 240 min, respectively.     

Inhibited intracrystalline cracks and enhanced electrochemical properties of NCM811 cathode materials coated by EPS

The formation of micro-cracks in Ni-rich LiNi_0.8Co_0.1Mn_0.1O₂ (NCM811) cathode particles is an extremely important factor affecting the electrochemical characteristics after long-term cycling. Generally, cracks can be divided into intergranular crack and intracrystalline crack according to their positions. Coating has been confirmed as a highly effective strategy to relieve intergranular cracks. However, the intracrystalline cracks of primary-like particles have rarely been studied. In this work, ethoxy functional polysiloxane (EPS) was directly coated on the surface of original NCM811 by tetraethyl orthosilicate (TEOS) hydrolytic polycondensation method without any additives. Then, the microstructure, micromorphology, surface state and electrochemical properties were investigated in detail by XRD, SEM, TEM, CV and EIS. The results displayed that the micro-cracks of primary-like particles were effectively suppressed under appropriate EPS coating. Accordingly, excellent capacity retention of 95.6% (100 cycles, 1C) and rate performance (144.6 mA h/g, 5C) were obtained. These improved mechanical and electrochemical properties are considered to be related to the EPS stress buffer layer, suppressed oxygen vacancies, inhibited phase transition and reduced volume change.     

Optimized microwave absorption properties by tailoring the morphology of carbon coated TiC nanoparticles by N2 pressure

Increasing the dielectric loss capacity plays an important role in enhancing the electromagnetic absorption performance of materials. It remains a challenge to simultaneously introduce multiple types of dielectric losses in the material. In this work, we show that the atomic and interfacial dipole polarizations can be simultaneously enhanced by substituting N species into both carbon coating layers and bulk TiC lattices of a core-shell TiC@C material. Additionally, substitution of N species results more exposed TiC(111) facets and refines the TiC grain sizes in the bulk material, which is beneficial for enhancing the scattering of the external electromagnetic waves. The maximum reflection loss of the N substituted TiC@C material is measured as ?47.1 dB with an effective absorbing bandwidth of 4.83 GHz at 1.9 mm, which illustrates a valuable way to further tuning the electromagnetic absorption performance of this type of materials.     

Effect of LiTFSI and LiFSI on Cycling Performance of Lithium Metal Batteries Using Thermoplastic Polyurethane/Halloysite Nanotubes Solid Electrolyte

All-solid-state lithium batteries(ASSLB) are promising candidates for next-generation energy storage devices.Nevertheless,the large-scale commercial application of high energy density AS S LB with the polymer electrolyte still faces challenges.In this study,a thin solid polymer composite electrolyte(SPCE) is prepared through a facile and cost-effective strategy with an infiltration of thermoplastic polyurethane(TPU),lithium salt(LiTFSI or LiFSI),and halloysite nanotubes(HNTs) in a porous framework of polyethylene separator(PE)(TPU-HNTs-LiTFSI-PE or TPU-HNTs-LiFSI-PE).The composition,electrochemical performance,and especially the effect of anions(TFSI~-and FSI~-) on cycling performance are investigated.The results reveal that the flexible TPU-HNTs-LiTFSI-PE and TPU-HNTs-LiFSI-PE with a thickness of 34 μm exhibit wide electrochemical windows of 4.9 and 5.1 V(vs.Li+/Li) at 60℃,respectively.Reduction in FSI~-tends to form more LiF and sulfur compounds at the interface between TPU-HNTs-LiFSI-PE and Li metal anode,thus enhancing the interfacial stability.As a result,cell composed of TPU-HNTs-LiFSI-PE exhibits a smaller increase in interfacial resistance of solid electrolyte interphase(SEI) with a distinct decrease in charge-transfer resistance during cycling.Li|Li symmetric cell with TPU-HNTs-LiFSI-PE could keep its stable overpotential profile for nearly 1300 h with a low hysteresis of approximately39 mV at a current density of 0.1 mA cm~(-2),while a sudden voltage rise with internal cell impedance-surge signals was observed within 600 h for cell composed of TPU-HNTs-LiTFSI-PE.The initial capacities of NCMITPU-HNTs-LiTFSIPEILi and NCMITPU-HNTs-LiFSI-PEILi cells were 149 and 114 mAh g~(-1),with capacity retention rates of 83.52% and89.99% after 300 cycles at 0.5 C,respectively.This study provides a valuable guideline for designing flexible SPCE,which shows great application prospect in the practice of ASSLB.